Upcycling Polypropylene Waste into Carbon Anode Materials for Lithium-Ion Batteries.

The growing accumulation of plastic waste is a serious environmental problem, and converting this waste into useful materials is an attractive solution. In this work, waste polypropylene (PP) was converted into hard carbon anode materials for lithium-ion batteries. When heated, PP decomposes into volatile hydrocarbons and leaves almost no solid residue, so it cannot be carbonized on its own. The waste PP was therefore first treated with concentrated sulfuric acid, which cross-links the polymer chains into a rigid, infusible network. This suppresses volatilization and promotes the formation of a thermally stable carbonaceous residue. The cross-linked material was then carbonized under argon at 700, 800, 900 and 1000 °C, and 22 to 24% of the original PP mass was recovered as carbon powder, depending on the carbonization temperature. X-ray photoelectron spectroscopy showed that the carbon surfaces retain 6.3-7.5 at% oxygen but almost no sulfur (≤0.2 at%), so sulfur is essentially absent from the final carbons. The carbonization temperature influenced the structure of the carbon and its performance in a battery. Among all samples, PP-900 delivered the highest reversible capacity at 0.1 A g