Investigation on FAB Morphology Evolution and Pd Redistribution Behavior in Palladium-Coated Copper Wires During Electronic Flame-Off (EFO) Process.
Article in Micromachines, 2026. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
5 authors.
Funding
Abstract
Compared with bare copper wire, palladium-coated copper (PCC) wire is widely used in microelectronic packaging due to its improved oxidation resistance and enhanced reliability. However, the formation mechanism of free air balls (FABs) and the redistribution behavior of Pd during the electronic flame-off (EFO) process, particularly under different Pd coating thicknesses and processing conditions, have not yet been fully understood. In this work, four types of 1 mil PCC wires with Pd coating thicknesses of 60, 80, 100, and 120 nm were systematically investigated to study the influence of EFO parameters on FAB morphology and Pd redistribution behavior. SEM, FIB, and EDS analyses were employed to provide experimental insights into the coupled relationship between transient thermal input, internal pore distribution and elemental segregation evolution, and Pd redistribution behavior. The results show that the preferred FAB morphology is obtained at 54 mA and 580 μs, with a diameter-to-wire ratio of approximately 2. With increasing Pd coating thickness, the exposed copper area on the FAB surface decreases from 13% to 6%, while the Pd-deficient region gradually shifts toward the bottom of the FAB. This study provides experimental insights into the Pd redistribution behavior during FAB formation under different EFO conditions, which may contribute to the optimization of Pd-coated Cu bonding wires.