Mechanical and Sustained-Release Properties of Crosslinked Poly(vinyl alcohol)/Sodium Humate Composite Membranes.
Article in Polymers, 2026. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
Abstract
Humic acid, as a natural macromolecular aggregate rich in functional groups, offers abundant modification sites and tunable chemical functionality, making it a promising building block for three-dimensional network construction. In this study, glutaraldehyde (GA) was employed as a crosslinking agent to incorporate sodium humate (NaHA, sodium salt of humic acid from alkaline treatment) into a polyvinyl alcohol (PVA) matrix, yielding composite membranes with enhanced structural stability and performance. The results demonstrate that NaHA effectively modulates the crosslinked network, and the physical and mechanical characteristics can be readily tailored by varying the PVA/NaHA/GA ratio. Compared with pristine PVA/GA hydrogel, the inclusion of NaHA significantly influences the mechanical response, with optimal comprehensive performance achieved at a NaHA content of 7.5 wt%, corresponding to a tensile strength of 60.4 MPa and an elongation at break of 74.2%. Furthermore, the cumulative release of NaHA after two days reached 64.4%, confirming that NaHA supramolecular aggregates were stably entrapped within the PVA/GA crosslinked matrix. The release kinetics were well described by the Korsmeyer-Peppas model. Overall, the covalent crosslinking of PVA with GA, together with hydrogen-bonding associations and physical entrapment mediated by NaHA, constructed a composite membrane network. This network exhibited tunable dry-state mechanical properties and sustained NaHA release, supporting its further evaluation as a prospective candidate for agricultural mulching films.