Integrating Flow Imaging Analysis and Single-Particle ICP-TOFMS for Comprehensive Micro- and Nanoplastic Characterization.

Flow imaging analysis (FIA), provides composition-agnostic morphological characterization. These measurements of particle size and shape are valuable to mass-based analysis, such as single particle inductively coupled plasma time-of-flight mass spectrometry (sp-ICP-TOFMS), which provides quantitative data on elements within particles. Using these two methods together enables informed use of geometric assumptions required by sp-ICP-TOFMS, as particle mass is typically converted to a particle diameter using assumed-spherical geometry. To validate this concept, parallel measurements to determine particle diameters were performed by FIA and sp-ICP-TOFMS on four particle suspensions: 300 nm polystyrene Eu-doped nanoparticles, 1 μm Fe-rich beads, 3 μm four element calibration polystyrene beads and 5 μm polystyrene beads. The Fe-particles obtained the highest percent difference from the manufacturer's nominal diameter, as the mean diameter obtained by FIA was overestimated by 21% and sp-ICP-TOFMS underestimated the mean diameter by 20.7%. Two types of particles were selected to test the effect of varying the particle number concentrations (PNC) on sizing accuracy, and both methods accurately sized each particle population at the PNC expected. Single particle analysis of carbon has continued to be a popular research topic, with direct applications to environmental pollutants in terms of nano- and micro- plastics. Real-world plastic particles were studied, and FIA's measured circularity values demonstrated that the particles deviated from spherical geometries, therefore sp-ICP-TOFMS data should be interpreted as mass-based rather than size-based. Combining these techniques enables improved interpretation of particle populations and evaluation of particle sizes.