The Characters of Second Phases and Texture of Aluminum Alloy Thin-Walled Capsule Welded Joints at Typical HIP Temperature.

Aluminum alloy capsules play a critical role in shape control, heat transfer, and pressure transmission during the PM-HIP sintering of Al-based powders. As the weakest part of the capsule, the reliability of the welded joint is crucial for the safe operation of the HIP process and the quality of the final product. This study investigated the effects of two typical HIP temperatures on the evolution of second phases and texture. The results show that: (1) At 400 °C, suppressed Si diffusion retains a continuous, low-melting-point Al-Si eutectic network and needle-like secondary phases in the weld zone, thereby impeding residual stress relief. Compositional segregation in the heat-affected zone weakens grain boundary stability. The texture undergoes only limited recovery, with a strong <100> orientation retained and micro-strain not effectively relieved, restricting joint ductility. (2) At 510 °C, Si is sufficiently spheroidized, forming a bead-like structure. Needle-like second phases transform into globular/short-rod morphologies, disrupting the continuity of the brittle phases. Simultaneously, complete recrystallization is induced, resulting in a randomized texture and significant release of micro-strain, thereby improving microstructural homogeneity and plastic deformation capacity. This study suggests that the internal stress concentration arising from the low-melting-point eutectic phase and strong texture poses a failure risk for the capsule. Therefore, employing the 510 °C HIP process to achieve second-phase spheroidization and texture weakening can significantly mitigate this failure risk.