Biaxial Cyclic Loading Test for Bauschinger Effect Characterization of Q890 High-Strength Steel.

Large-scale thick curved components made of high-strength steel are critical to deep-sea pressure hulls and large structural components of engineering machinery. During forming, these components experience reverse loading upon unloading, and the pronounced Bauschinger effect of high-strength steel significantly compromises springback prediction accuracy, leading to costly die iterations. Existing cyclic tension-compression and shear tests are limited to uniaxial stress states and fail to capture the mechanical behavior under in-plane biaxial cyclic loading. Herein, a cyclic four-point bending method is proposed to characterize the Bauschinger effect of Q890 steel under biaxial cyclic loading. By tailoring the width-to-thickness ratio of the specimens, a series of plane stress states with different initial plastic stress ratios were obtained, covering the dominant stress conditions encountered in forming typical large-scale double-curvature thick plates. Full-field strain evolution during cyclic bending was captured in real time via digital image correlation (DIC), enabling systematic acquisition of equivalent stress-strain curves under various biaxial stress ratios over multiple cycles. As the width-to-thickness ratio increases, both forward and reverse yielding progressively degrade: the equivalent yield strength, forward peak flow stress, and reverse yield strength drop from 1098, 1193, and 742 MPa to 934, 1065, and 685 MPa, respectively. Accordingly, the Bauschinger ratio B, Bauschinger hardening parameter BHP, and Bauschinger energy parameter BEP decrease from 0.479, 0.789, and 4.747 to 0.363, 0.655, and 2.900, respectively, revealing a strong stress-ratio dependence of the Bauschinger effect. Notably, the springback ratio also shows clear dependence on the biaxial stress ratio, loading direction, and cyclic history, indicating that in-plane biaxial stress-state effects should be considered when characterizing the Bauschinger effect and springback behavior of Q890 high-strength steel.