Investigation into the Storage-Induced Oxidation Mechanism of Prussian Blue Analogues.

This study reports the synthesis of low-defect Prussian blue analogues (PBAs) using a single iron-source method and systematically investigates the influence of atmospheric components, particularly water and oxygen, on their oxidative decomposition. Our findings demonstrate that the oxidative degradation of PBAs is governed synergistically by moisture and oxygen, with ambient humidity identified as the primary factor determining both the extent and kinetics of their decomposition. Notably, a pure oxygen environment by itself does not trigger material degradation, while oxygen markedly accelerates the decomposition only in the presence of moisture. As a result of the oxidation, enhanced Coulombic interaction between sodium ions and cyano groups induces structural modifications in the lattice framework, driving a phase transformation from monoclinic to cubic symmetry, accompanied by changes in its unit cell volume. Furthermore, in high-humidity environments, atmospheric moisture promotes the gradual deintercalation of sodium ions from the Prussian blue framework, resulting in the conversion of sodium-rich Prussian blue to the sodium-deficient form. Concurrently, an increase in lattice defect density leads to partial structural collapse, inducing the release of free ferrocyanide ions, which may subsequently react with the deintercalated sodium ions to form the sodium ferrocyanide impurity phase. We also find that the preferential decomposition of low-spin iron over high-spin iron within the framework leads to a further reduction in its electrochemical capacity. In contrast, potassium Prussian blue exhibits minimal interaction with water molecules and can effectively repel them through steric hindrance. Therefore, partial substitution of sodium with potassium ions is proposed as a viable strategy to enhance the structural stability of the Prussian blue framework, improve the storage performance of sodium Prussian blue (NaPB), and mitigate water ingress. This work offers fundamental insights into the storage characteristics and oxidative degradation mechanisms of PBAs.