Validated Reactive Force Field Quantifies MXene Interfacial Properties, Mechanics, and Thermal Transport.

MXenes combine rich surface chemistry, mechanical strength, and high conductivity for a multitude of emerging applications. Predictive modeling supports accelerated materials designs and has been limited by the absence of validated and transferable force fields. Here, we introduce an interpretable, reactive INTERFACE force field (IFF and IFF-R) for Ti3C2Tx MXenes that is trained based on chemical knowledge and achieves quantitative agreement with experiments across lattice parameters (<0.5%), density (<0.2%), liquid contact angles, Raman spectra, and the in-plane elastic modulus (∼320 GPa). The models cover surface terminations from hydroxyl (-OH) to fluorine (-F) groups and are extensible to other chemistries. We introduce pH-resolved surface chemistry and identify dopamine adsorption mechanisms at MXene-aqueous interfaces supported by QCM-D and UV-Vis experiments. The data reveal coplanar and perpendicular binding modes and concentration-dependent multilayer assembly. We predict previously inaccessible properties, including termination-dependent cleavage energies, interlayer shear moduli and dynamic shear failure, nanoindentation and brittle fracture, anisotropic in-plane and out-of-plane thermal conductivities, including the role of defects. Agreement with available experimental data is consistently close and exceeds DFT accuracy across the benchmark properties examined. The IFF/IFF-R model is compatible with CHARMM, AMBER, OPLS, and CVFF force fields for simulations of MXenes with diverse surface terminations, electrolyte interfaces, biointerfaces, and polymer composites without additional parameters. Parameter sets, 3D models, and analysis scripts are provided for community use. The validated, reactive, and transferable IFF framework facilitates predictive design of MXene-based films, membranes, sensing interfaces, and composites.