Flexible Compostable Composite Films Based on Plasticized Reprocessed PLA and Reinforced with Rice Husk and Rice Husk Biochar.

In this study, the valorization of poly(lactic acid) (PLA) waste as well as rice husk into sustainable materials was explored. To simulate the industrial valorization of defective PLA parts, scraps and burrs, PLA was reprocessed (rPLA) by melt extrusion and further plasticized with 15 wt.% of acetyl tributyl citrate (ATBC) and reinforced with rice husk (RH) or rice husk biochar (RHB) in 1 or 3 wt.%. The melt flow index was determined to assess the effect of reprocessing and the addition of RH or RHB on the material degradation. The obtained films were characterized in terms of their structural, mechanical, and thermal behavior. The water-related behavior of the materials was evaluated by measuring the static water contact angle and the water vapor transmission rate (WVTR). Compostability was proposed as an end-of-life option, therefore disintegration under composting conditions was assessed. Reprocessing increased the MFI and slightly reduced the strength and the modulus, consistent with chain scission. ATBC facilitated the processability, improved the particles' dispersion and provided ductility to the final materials. RH and RHB acted mainly as nucleating agents and strongly modified the surface wettability. A low RHB loading improved the WVTR, whereas a higher filler content and ATBC generally increased the WVTR. All the films were completely disintegrated within 18 to 21 days. These results show practical valorization routes to obtain rPLA films with tunable properties and to preserve the inherent composting disintegration of PLA.