Comparative Mechanical and Thermal Performance of Graphene- and Silver Nanoparticle-Reinforced PLA Fabricated by FDM 3D Printing.

The increasing demand for high-performance and multifunctional polymer materials has driven interest in improving the mechanical properties of polymer components produced through additive manufacturing. This study aims to systematically investigate and comparatively evaluate the effects of low-content nanofiller incorporation on the structural, thermal, and mechanical performance of PLA-based materials produced via fused deposition modeling (FDM), with a focus on identifying filler-dependent behavior under different loading conditions. In this study, polylactic acid (PLA) composites reinforced with 0.5 wt.% graphene (Gr) and 0.5 wt.% silver (Ag) nanoparticles, added separately, were produced using fused deposition modeling (FDM) and comparatively investigated. Each nanofiller was incorporated individually into PLA-based filaments, and standard test specimens were fabricated via 3D printing. Structural, thermal, and mechanical properties were evaluated using tensile, compressive, and three-point bending tests, along with SEM, EDS, XRD, FTIR, DSC, and TGA analyses. The results showed that pure PLA exhibited typical brittle behavior and a single-stage thermal degradation profile. The tensile strength of pure PLA was 41.93 MPa, and the flexural strength was 70.76 MPa. The addition of 0.5 wt.% graphene led to noticeable improvements, particularly in flexural properties, while only a minimal (almost negligible) increase was observed in tensile strength, with tensile strength increasing to 42.24 MPa (+0.74%) and flexural strength increasing to 110.78 MPa (+56.6%). In contrast, 0.5 wt.% Ag exhibited mixed and load-dependent mechanical behavior, with slight improvements in flexural strength but reductions in tensile and compressive properties, where tensile strength decreased to 22.13 MPa (-47.2%) while flexural strength increased to 112.06 MPa (+58.3%). Structural and thermal analyses indicated that both nanofillers did not significantly alter the PLA matrix chemically, while contributing to controlled changes in material properties primarily through physical interactions. The novelty of this work lies in the comparative evaluation of graphene and silver nanoparticle reinforcement at a fixed low loading level within FDM-processed PLA, combined with a comprehensive and correlated analysis of mechanical, structural, and thermal behavior on the same specimen sets, enabling a clearer understanding of filler-dependent performance mechanisms in additively manufactured nanocomposites. Overall, it was concluded that low-rate nanofiller additions, when properly dispersed, may lead to selective improvements in the performance of PLA-based composites depending on filler type and loading mode, and show potential for advanced engineering applications such as lightweight structural components, functional sensors, and additive-manufactured parts requiring tailored mechanical performance and multifunctionality.