Synergistic Role of Crosslinker and Silane-Based Additive in Designing Structurally Robust Bio-Based Polyurethane Coatings.

Bio-based polyurethane (PU) coatings offer sustainable alternatives to petrochemical coatings but often suffer from inferior mechanical performance, durability, and chemical resistance. This work addresses that challenge by integrating a trifunctional bio-based crosslinker (glycerol) and a silane-based additive (hexamethyldisilane (HMDS)) to simultaneously enhance structural robustness and hydrophobicity. Coatings were synthesized using a renewable soybean oil polyol (SOP), glycerol (5, 10, 15 and 20 wt.%), and methylene diphenyl diisocyanate (MDI), followed by the addition of HMDS (10, 20, 30, 40 and 50 wt.%). Mechanical tests identified 10 wt.% glycerol as the optimal content, yielding a maximum tensile strength of 47.18 MPa. Incorporating 10 wt.% HMDS into the optimized formulation greatly increased water contact angle (WCA, 95.76°) and chemical resistance with minimal loss of mechanical performance (38.19 MPa, tensile strength); higher HMDS loadings caused network disruption and reduced strength. Calorimetry and thermogravimetric analyses confirmed that the modified coatings retained high thermal stability. This synergistic crosslinker additive strategy produced a structurally robust, water-resistant bio-based coating, demonstrating a viable high-performance sustainable coating solution for industrial applications.