Thermoreversible Diels-Alder Crosslinked Networks in Recycled Poly(ethylene terephthalate) for Reprocessability and Self-Healing.
Article in Polymers, 2026. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors.
Funding
Abstract
A thermoreversible dynamic covalent network was constructed in recycled polyethylene terephthalate (RPET) via Diels-Alder (DA) chemistry to enhance mechanical performance, reprocessability, and self-healing. Furan-functionalized RPET (RPET-3F) was first prepared from maleated RPET (RPET-MA), followed by crosslinking with bismaleimide (BMI) at different feed ratios. FTIR spectra confirmed the successful grafting of furan groups and the formation of DA adducts. With increasing BMI content, the gel fraction and crosslink density increased substantially, whereas the swelling ratio decreased, indicating the progressive development of a three-dimensional network. RPET-3F-2B showed the highest network integrity among all samples. DSC analysis revealed a distinct retro-DA dissociation peak at 143 °C and a recrosslinking peak near 124 °C, confirming the thermal reversibility of the DA network. Owing to the optimized network structure, RPET-3F-2B exhibited the best mechanical properties and excellent reprocessability, retaining stable performance after three hot-pressing cycles. After repeated reprocessing, its tensile strength remained 74% higher than that of RPET-MA, while the elongation at break was still improved by about 10%. Moreover, the sample showed efficient thermally induced self-healing at 150 °C, with surface cracks nearly disappearing after 4 h. These results demonstrate that DA chemistry offers a promising route to the high-value reutilization of RPET into recyclable, multifunctional polymer materials.