Removal of Congo Red Dye from Aqueous Solution via Natural Seeds Integrated with Zinc Oxide-Doped Manganese Ferrite.

This study reports the preparation of a nanocomposite using a black cumin surface as a carbon framework on which zinc oxide-doped manganese ferrite nanoparticles were deposited and grown. A simple precipitation method was used to prepare the nanocomposite. The resulting composite was characterized using various characterization analyses such as FTIR, XRD, EDX, SEM, TEM, and TGA. The composite surface was highly conformed with functional groups, and the nanocomposite was formed due to electrostatic and non-electrostatic interactions between the carbon framework and the nanoparticles. X-ray analysis revealed a crystalline structure with crystal sizes up to 45 nm. Microscopic images revealed the surface morphology, confirming the irregular distribution of particles within the composite. The resulting composite material was used for adsorption application. The composite material was tested for the removal of Congo red dye from water. It was found that under optimal conditions, a dose of 2 g per liter of absorbent removed nearly 100% of dye from a 10 mL volume of 10 mg per liter Congo red solution within 90 min and 7 pH. A monolayer adsorption was confirmed by the isotherm analysis. The monolayer adsorption capacity for the present study was ~13.0 mg per gram. The adsorption kinetics suggested the fitting of pseudo-second order. Based on the findings, it was concluded that the chemical mechanism was responsible for the present adsorption process. The regeneration study demonstrates the stability of current adsorbent up to two cycles only. This nanocomposite is the first of its kind which promotes the creation of nanocomposites in the future by using natural materials and reduces the dependency on activated carbon.