Deconstructing Multi-Scale Hybrid Fiber-Reinforced Coarse Aggregate UHPC: From Pore Structure Tailoring to Cross-Scale Toughening.

Ultra-high-performance concrete incorporating coarse aggregates (UHPC-CA) exhibits pronounced multi-scale heterogeneity and staged damage evolution. However, existing single-scale reinforcement strategies often fail to address the complete micro-to-macro fracture process, leaving a critical research gap in achieving full-stage crack control. To address this, this study introduces a novel cross-scale toughening strategy using hybrid steel fibers (SF) and calcium carbonate whiskers (CCW), and decouples the coupled influences of water-to-binder (W/B) ratio, coarse aggregate (CA), and multi-scale fibers via an orthogonal design. Mechanical properties, fiber dispersion, and pore structure are jointly characterized to establish structure-property relationships. An optimal composition (W/B = 0.32, CA = 18%, SF = 2%, CCW = 1%) is identified, achieving a balanced enhancement of strength and ductility. Results indicate that matrix densification is primarily controlled by W/B via pore refinement, while mechanical performance is governed by the interplay between fiber spatial uniformity and interfacial integrity; the roles of CA and CCW are clearly stress-state dependent. Furthermore, a novel cross-scale synergistic mechanism is revealed, in which micro-scale CCW regulates microcrack initiation and stabilizes the pre-peak response, whereas macro-scale SF dominates post-peak behavior through crack bridging and pull-out energy dissipation. This sequential activation enables a full-stage enhancement of tensile performance, shifting failure from brittle localization to pseudo-ductile multiple cracking. The findings provide a correlative framework for tailoring UHPC-CA through multi-scale hybrid reinforcement.