Influence of Particle Size and Mineralogical Composition on the Mechanical and Tribological Properties of Resin-Regolith-Composites for Non-Structural Applications.
Article in Materials (Basel, Switzerland), 2026. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
3 authors.
Funding
Abstract
The development of resin-regolith composites represents a promising In Situ Resource Utilization (ISRU) strategy for future lunar missions. While unsuitable for primary habitat construction due to the payload cost of transporting polymers from Earth, these composites offer a highly efficient solution for manufacturing non-structural, everyday items (e.g., containers, tools, and plant cultivation pots) directly on the Moon via mold-casting. This approach significantly reduces the volume and mass of pre-formed plastic payloads. In this work, the influence of the particle size distribution of a lunar highland simulant (LHS-1E) on the mechanical properties of epoxy-based composites was systematically investigated for such applications. First, the regolith-to-resin ratio was optimized for castability, establishing a maximum regolith content of 60 wt.%. Then, four different size fractions of the simulant were prepared by sieving (>200 µm, 200-100 µm, 100-50 µm, and <50 µm), and composite samples were cast maintaining this optimal ratio. X-ray microtomography revealed that using larger particles (>200 µm) increased composite porosity, whereas smaller fractions promoted more compact structures. Three-point bending tests showed that intermediate particle sizes (200-100 µm and 100-50 µm) led to enhanced flexural strength, while the smallest particles (<50 µm) decreased mechanical performance, likely due to a lower basalt content in this finer fraction. Finally, ball-on-disk tribological analyses highlighted that composites made with larger particles (>200 µm) exhibited superior wear resistance, whereas particle size had negligible effects on the coefficient of friction. Overall, the results demonstrate that both particle size and mineralogical composition significantly influence the performance of regolith-epoxy composites, providing essential guidelines for the in situ manufacturing of functional, non-structural objects for lunar outposts.