Research on Microstructure and Properties of Ultrasonic Welded Large-Diameter Aluminum Wire/Cu (Ni-Plated Copper) Terminal Joints.

In this study, the microstructure and mechanical properties of ultrasonic welded joints between large-diameter aluminum wire and Cu (Ni-plated copper) terminals were systematically investigated, to reveal the underlying fracture mechanisms. The cross-sectional morphology, interfacial microstructure, and mechanical properties of the two types of welded joints are investigated. The results indicate that ultrasonic welding produces well-structured Al-Cu and Al-Ni joints. Under the same welding process parameters, the Al-Cu joint exhibits many pores, while the Al-Ni joint has no pores in its microstructure. The interfacial region of the Al-Cu joint presents various morphologies, such as flat bonding, interlocking, and eddy current patterns, whereas the Al-Ni joint interface is flat. No significant atomic diffusion phenomenon occurs between the interfaces of the two types of joints. The tensile strength of the Al-Cu joint is 53 MPa, with fracture modes including ductile fracture and brittle fracture, whereas the tensile strength of the Al-Ni joint is 50 MPa, with a failure mode of pull-out fracture. In working conditions requiring ultrasonic welding of aluminum and copper, nickel-plated copper can be used as a substitute for copper to prevent electrochemical corrosion between aluminum and copper.