Investigation on the Microstructure and Mechanical Properties of 304 Stainless Steel Joints by Underwater Local Dry Laser Welding.
Article in Materials (Basel, Switzerland), 2026. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
8 authors.
Funding
Abstract
In order to verify the feasibility of in situ repair of underwater local dry laser welding (ULDLW) on nuclear power reactor components, this work investigates the microstructure and mechanical properties of 304L austenitic stainless steel repaired by ULDLW using ER308L filler metal. Comprehensive comparison would be made between the ULDLW and conventional in-air laser welding to evaluate their applicability. The results demonstrate that the rapid cooling rate inherent to the underwater environment significantly influences solidification behavior and microstructural evolution. The weld metal (WM) solidifies in the ferritic-austenitic (FA) mode, with an increased proportion of lathy δ-ferrite at the expense of skeletal morphology compared to the in-air welds. Electron backscatter diffraction (EBSD) analysis reveals the substantial grain refinement in underwater welds, with average grain sizes of 39.4 μm versus 47.3 μm for in-air weld bead, accompanied by a higher fraction of low-angle grain boundaries (LAGBs). These microstructural modifications yield superior mechanical properties: underwater weld bead exhibits ultimate tensile strength (UTS) of 685.6 MPa, elongation of 57.5%, and impact toughness of 22.6 J, significantly exceeding the corresponding values for in-air welds (663.9 MPa, 51.8%, and 18.6 J, respectively). Fractographic analysis confirms ductile fracture mechanisms in both conditions. The enhanced performance is attributed to grain refinement strengthening via the Hall-Petch relationship and the increased LAGBs fraction, which impedes dislocation motion and crack propagation.