Research on Plasma Characteristics of High-Power Impulse Magnetron Sputtering Ti-Nb-Cr Target and Its Effect on Film Properties.
Article in Materials (Basel, Switzerland), 2026. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
- Design of Experiments for the Study of High-Power Pulsed Magnetron Sputtering.Materials (Basel, Switzerland) · 2026Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
Abstract
High-power impulse magnetron sputtering (HiPIMS) technology was used to deposit Ti-Nb-Cr films on Si (100) and 316L substrates by changing the peak power of the Ti-Nb-Cr target. Optical emission spectroscopy (OES) was used to study the effect of peak power on the ion atomic arrival ratio in front of the substrate. Experimental instruments such as an X-ray diffraction (XRD) device, scanning electron microscope (SEM), transmission electron microscope (TEM), nanohardness tester, ball-disk reciprocating friction machine, and electrochemical workstation were used to study the effects of the atomic arrival ratio of Ti, Nb, and Cr ions on the microstructure, mechanical properties, and corrosion resistance of Ti-Nb-Cr films. The results show that when the peak power is 67.84 kW, the ion atomic arrival ratio of Ti reaches 47.57%, the ion atomic arrival ratio of Nb reaches 39.41%, and the ion atomic arrival ratio of Cr reaches 10.6%. The ion atomic arrival ratio is doubled compared to the peak power of 51.04 kW. The films prepared at different peak powers all show diffraction peaks of the BCC structure. At high power levels, the TiNbCr films exhibit reduced residual compressive stress, although this may be accompanied by lower hardness and wear resistance.