An Investigation into the Friction Stir Spot Welding Behavior of 3D-Printed Glass Fiber-Reinforced Polylactic Acid.
Article in Polymers, 2026. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
3 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
The production of fiber-reinforced polymer composites using 3D printing technology offers significant potential and opportunities for industrial applications. However, current dimensional limitations in 3D printing necessitate the use of joining techniques to obtain larger components. Recently, innovative strategies such as friction stir spot welding (FSSW) have attracted considerable attention for joining polymer composites due to their ability to produce strong joints with relatively low heat input (solid-state welding). Nevertheless, it is important to understand how the fibers present in fiber-reinforced polymer composites influence material flow and welding performance during the FSSW process. In this study, glass fiber-reinforced polylactic acid (PLA-GF) composite samples produced using a 3D printer were joined by means of FSSW. Five different tool rotational speeds (900, 1200, 1500, 1800, and 2100 rpm) and three different plunge rates (10, 20, and 30 mm/min) were employed during the welding process. Mechanical tests were performed on the welded joints to investigate the relationship between the welding parameters and the resulting mechanical properties. In addition, microstructural analyses were conducted to examine the formation of welding defects. The results revealed that three distinct zones were formed in the material after the FSSW process: the stir zone, mixed zone, and shoulder zone. Defects were observed in the mixed zone of the samples exhibiting relatively lower mechanical properties. The highest tensile force was achieved at a plunge rate of 20 mm/min and a rotational speed of 900 rpm. The highest bending force, on the other hand, was obtained at a plunge rate of 30 mm/min and a tool rotational speed of 2100 rpm.