A comparative analysis of the effects of green blended activators on the durability and mechanical performance of slag-based geopolymer cement.
Article in Scientific reports, 2026. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
4 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Investigating environmentally suitable alternatives becomes crucial as demand for Portland cement is expected to increase dramatically over the next several years. Alkaline-activated binders produced by alkali activation of aluminosilicate precursors serve as greener and viable substitutes for PC. However, conventional activators such as sodium silicate (SS) or sodium hydroxide (NaOH) are corrosive, costly, and pose significant environmental concerns. In contrast, sodium carbonate (Na2CO3, NC) and calcium carbonate (CaCO3, CC) are less corrosive, more affordable, and naturally abundant, making them sustainable alkali activators for AAs. To advance the use of sustainable binders, this study investigated the properties of slag activated with a blended activator composed of Na2SiO3/Na2CO3 or Na2SiO3/CaCO3 at room temperature. The findings reveal that using a combined activator of SS and CC reduces compressive strength and delays the setting process, whereas a blend of SS and NC improves strength by 10 to 12% over a curing period of 3–90 days. Additionally, using a blend of 7% SS + 3% NC as an activator reduces total porosity and water absorption and improves the highest bulk density. Under 5% MgSO₄ attack for six months, CC-containing mixes deteriorated severely (strength decreased to 3.1–15.4 MPa), whereas NC-activated mixes retained higher strength (34.4–40.6 MPa). After firing at 300, 600, and 800 °C, M5 retained approximately 70%, 51%, and 39% of its original 28-day strength, respectively, outperforming CC-based systems (32–84% loss). XRD, FTIR, and SEM analyses confirmed denser C–A–S–H and/or N–A–S–H gel formation in SS/NC mixes. The findings demonstrate that Na₂CO₃ is a technically viable, environmentally safer, and economically attractive partial substitute for sodium silicate, delivering enhanced durability and thermal resistance for sustainable structural applications.