Ultrasonic Testing of Laser Welds in Medium-Thick Titanium Alloy Plates.

To address the challenge of detecting internal defects in medium-thick titanium alloy laser welds, a combined simulation and experimental study on ultrasonic testing was conducted. A finite element model employing a 5 MHz shear wave angle transducer for inspecting titanium alloy welds was established. An ultrasonic testing system was developed, incorporating a DPR300 pulser-receiver (JSR Ultrasonics, Pittsford, NY, USA) and an MSO5204 oscilloscope (RIGOL, Suzhou, China), and was calibrated using standard reference blocks. The inspection results for four prefabricated internal defects at various depths demonstrated that all defects were effectively detected, with the minimum detectable equivalent defect size reaching 1 mm. The measured signal-to-noise ratio (SNR) averaged 17.6 dB, validating the high sensitivity of the proposed system. The mean absolute error for defect localization was 0.438 mm, achieving a positioning accuracy better than 0.5 mm. This study indicates that the pro-posed method enables effective detection and accurate localization of internal defects in titanium alloy laser welds, providing critical technical support for laser welding quality assessment.