The Effect of PDMS Incorporation on the Physicochemical Properties of Acrylate-Based Resins for SLA-Based 3D Printing.
Article in Polymers, 2026. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
5 authors.
Funding
Abstract
A photo-curable silicone-modified resin system based on polydimethylsiloxane (PDMS) was developed and systematically evaluated for stereolithography (SLA)-based 3D printing applications. The resin formulation consisted of bisphenol A ethoxylate dimethacrylate (Bis-EMA) and trimethylolpropane triacrylate (TMPTMA) as reactive monomers, with methacrylate-terminated PDMS (PDMS-MMA) incorporated at concentrations ranging from 0 to 15 wt%. The influence of PDMS-MMA content on key physicochemical properties relevant to SLA processing, including viscosity, mechanical performance, thermal stability, optical transmittance, and curing shrinkage, was systematically investigated. Moderate incorporation of PDMS-MMA improved the mechanical flexibility of the resin, with the tensile strength reaching a maximum value of 5.95 MPa at 5 wt% PDMS-MMA. However, further increases in PDMS-MMA content resulted in a gradual decrease in tensile strength and optical transmittance, indicating the importance of optimizing the formulation composition. Thermogravimetric analysis (TGA) indicated improved thermal stability with increasing PDMS-MMA content, while curing shrinkage decreased progressively as the PDMS fraction increased. Structural printing tests confirmed that the developed resin system exhibited stable layer adhesion and shape fidelity during SLA fabrication, enabling the successful printing of complex three-dimensional structures. These results demonstrate that PDMS-modified acrylate resins provide a promising strategy for balancing mechanical flexibility, dimensional stability, and printability in SLA-based additive manufacturing.