PVA-KH792-Enhanced Composite Cementitious Material from Lead-Zinc Slag and Electroplating Sludge: Mechanical Performance and Heavy-Metal Immobilization.
Article in Materials (Basel, Switzerland), 2026. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
2 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
To address the limited simultaneous optimization of mechanical performance and heavy-metal stabilization in waste-based alkali-activated systems, this study investigates the development and characterization of a novel composite cementitious material for potential construction applications, utilizing lead and zinc smelting slag (LZSS) and electroplating sludge (ES) as precursors. The novelty of this study lies in the co-modification of an LZSS-based alkali-activated matrix with PVA and KH792 to improve both compressive behavior and heavy-metal stabilization in ES-containing specimens. Based on single-factor optimization, the optimal matrix was obtained at 3.5% alkali content, a water-glass modulus of 1.4, and a liquid-to-solid ratio of 0.22, followed by 28 days of curing before testing. On this basis, ES and PVA-KH792 were introduced to investigate their effects on mechanical behavior, heavy-metal leaching, and immobilization mechanisms. The results showed that adding ES reduced the compressive strength of the alkali-activated matrix, whereas PVA-KH792 modification partially restored matrix integrity and improved performance. At 5% ES content, the compressive strength of the modified specimen increased by 7.66% compared with that of the unmodified ES-containing sample. More importantly, under the sulfuric acid-nitric acid leaching method, the Cr leaching concentration decreased from 20.1 mg/L to 13.7 mg/L, meeting the relevant regulatory limit (GB5085.3-2007 and EPA limit). Microstructural and spectroscopic analyses indicated that the beneficial effect of PVA-KH792 was associated with matrix densification and enhanced heavy-metal immobilization. The immobilization mechanisms were mainly attributed to Cr(VI) reduction by Fe(II), complexation/coordination with functional groups introduced by PVA-KH792, and physical encapsulation within the alkali-activated matrix. The findings provide a promising approach to waste valorization and the development of sustainable building materials, contributing to resource efficiency and reducing the environmental impact of the construction sector.