Investigation of Thermal-Microstructure-Hardness Relationships in Dissimilar AA5052-H32/AA6061-T6 Friction Stir Welded Joints.
Article in Materials (Basel, Switzerland), 2026. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
4 authors.
Funding
Abstract
Friction stir welding (FSW) of dissimilar aluminium alloys often results in non-uniform microstructure and hardness distributions due to asymmetric temperature fields and material flow. The objective of this study is to establish a quantitative relationship between thermal history, microstructural evolution, and hardness distribution in dissimilar AA5052-H32/AA6061-T6 FSW joints by combining experimental characterisation with validated thermal modelling. AA5052-H32 and AA6061-T6 plates were welded under five different parameter sets. A thermal finite element model was developed in COMSOL Multiphysics to simulate temperature evolution during welding and was validated using embedded thermocouple measurements, with predicted peak temperatures ranging from 455 °C to 641 °C. Optical microscopy, scanning electron microscopy (SEM), and electron backscatter diffraction (EBSD) were employed to characterise grain structure and dynamic recrystallisation (DRX) behaviour, while Vickers microhardness mapping was used to evaluate the local mechanical response. The results show that DRX occurred in the nugget zone (NZ), leading to significant grain refinement, with a minimum grain diameter of 6.07 µm, representing an approximately eightfold reduction compared with the base material AA5052-H32. In contrast, the thermo-mechanically affected zone (TMAZ) experienced limited recrystallisation due to insufficient plastic deformation and temperature. The lowest hardness was observed in the TMAZ on the AA5052-H32 side, with the hardness reduction of 22% primarily caused by work hardening loss. Hardness was also reduced by 34% on the AA6061-T6 side due to decreased precipitation strengthening caused by high temperatures. This combined experimental-numerical study provides a systematic thermal-microstructure-hardness framework for understanding and predicting local property variations in dissimilar FSW joints.