Rationally Designed PU/CNFs/ZIF-8/PANI Composite Foams with Enhanced Flexibility and Capacitance for Flexible Supercapacitors.

Benefiting from their outstanding porosity, considerable specific surface area, and natural flexibility, cellulose nanofibers (CNFs)/MOF materials have emerged as competitive candidates for advanced flexible energy storage devices. However, conventional CNFs/MOFs aerogels or films often suffer from poor recoverability under compression, bending, and folding, accompanied by severe plastic deformation that compromises the cycling and structural stability of devices. To address this issue, we report a rationally designed flexible PU/CNFs/ZIF-8/PANI composite foam with an interconnected micro-mesoporous structure. Using polyurethane foam as a soft substrate and CNFs/ZIF-8 as building blocks, the composite was fabricated through a combined strategy of impregnation, in situ ZIF-8 growth, hot-pressing, and in situ aniline polymerization with simultaneous etching of the ZIF-8. The incorporation of carboxylated CNFs enhances the hydrophilicity of the PU skeleton. This, in combination with the hot-pressed framework, establishes an interconnected 3D network, thereby effectively preventing the agglomeration of active materials. Meanwhile, the hierarchical pores derived from the sacrificial ZIF-8 template provide abundant electroactive sites, accelerate ion transport, and facilitate high PANI loading. By virtue of this synergistic architectural effect, the resultant electrode achieves a high specific capacitance of 449 F/g at 0.2 A/g, with 97% capacitance retention after 2000 cycles at 5 A/g. Furthermore, the composite foam demonstrates excellent mechanical flexibility, with a tensile strength of 0.87 MPa and an elongation at break of 230%. This work offers a feasible approach for developing high-performance flexible supercapacitors and provides novel perspectives for the rational design of portable energy storage devices.