Processing-Microstructure-Property Relationships in a Cu-Rich FeCrMnNiAl High-Entropy Alloy Fabricated by Laser and Electron Beam Powder Bed Fusion.
Article in Materials (Basel, Switzerland), 2026. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
4 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
A Cu-containing FeCrMnNiAl multi-principal element alloy was processed by laser-based and electron beam-based powder bed fusion (PBF-LB/M and PBF-EB/M) to investigate processing-microstructure-property relationships. In focus were alloy variants with a relatively high Cu content. Two PBF-LB/M scan strategies, employing a Gaussian beam with and without a re-scan with a laser featuring a flat-top profile, were compared to PBF-EB/M processing, followed by heat-treatments between 300 °C and 1000 °C. The phase constitution, elemental partitioning and grain boundary characteristics were analyzed by X-ray diffraction, electron backscatter diffraction and energy-dispersive X-ray spectroscopy. Mechanical behavior was assessed by hardness and tensile testing. Both manufacturing routes promoted the evolution of stable multi-phase microstructures composed of face-centered-cubic (FCC)- and body-centered-cubic (BCC)-type phases across all heat-treatment conditions. PBF-LB/M processing resulted in finer, dendritic microstructures and suppressed formation of a Cu-rich FCC phase due to higher cooling rates, whereas PBF-EB/M promoted the evolution of Cu-rich FCC segregates and equiaxed grain morphologies. Heat-treatment above 700 °C led to recrystallization, accompanied by an increase of the FCC phase fraction, grain coarsening, and recovery. At lower heat-treatment temperatures, the changes in microstructure are different. Here, it is assumed that small, non-clustered Cu-rich precipitates formed at the grain and sub-grain boundaries, although this assumption is only based on the assessment of the mechanical properties. The size of these precipitates is below the resolution limit of the techniques applied for analysis in the present work. Additional structures seen within the Cu-rich areas of PBF-EB/M-manufactured samples treated at lower temperatures also seem to have an influence on the hardness and yield strength. All of the conditions investigated exhibited pronounced brittleness, limiting reliable tensile property evaluation and indicating the need for further optimization of processing strategies and microstructural control for high-Cu-fraction-containing multi-principal element alloys.