Structural and Mechanical Analysis of Individual Mineralized Collagen Fibrils Using In Situ Transmission Electron Microscopy.

Bone serves as an example of nature's architectured material with its characteristic blend of strength and toughness, all at a lightweight design. Given the hierarchical nature of these materials, it is essential to understand the governing mechanisms and organization of their constituents across length scales for bioinspired structural design. Despite recent advances in transmission electron microscopy (TEM) that have allowed us to witness the hierarchical arrangement of bone at micro-down to the nanoscale, we are still missing the details about the structural organization and mechanical properties of the main building blocks of bone─mineralized collagen fibrils (MCFs). Here, we present a method to extract individual MCFs from nature's model material, mineralized turkey leg tendon, using a dropcasting procedure. By isolating the MCFs onto TEM supporting grids, we visualized the arrangement of organic and mineral phases within individual MCFs at the nanoscale. Using a four-dimensional scanning transmission electron microscopy (4D-STEM) approach, the orientation of individual mineral crystals within the MCFs was examined. Furthermore, we conducted in situ tensile experiments, revealing exceptional tensile strains of at least 8%, demonstrating the intricate relationship between structural organization and the mechanical behavior of MCFs. These insights into the ultrastructure of mineralized tissue building blocks, as well as the proposed sample-extraction method compatible with in situ mechanical testing, provide a strong basis for research into nature-inspired material design.