Influence of Base Plate Preheating on Laser Powder Bed Fusion-Processed EN AW-7075 Aluminium Alloy.
Article in Materials (Basel, Switzerland), 2026. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
4 authors.
Funding
Abstract
The influence of base plate temperature (25, 100, 200, and 400 °C) on the laser powder bed fusion processing of EN AW 7075 was systematically investigated using microstructural characterisation (LM, SEM, EBSD, GROD), chemical analysis, hardness testing, and thermal simulations across a broad range of process parameters. Moderate preheating at 100 °C and 200 °C showed no significant reduction in crack density or changes in grain morphology compared to processing without preheating. At the highest studied temperature-400 °C-a transition to columnar crack networks was observed, accompanied by modified grain orientation, pronounced stress relaxation, and reduced hardness. Independent of preheating temperature, consistent evaporation of Zn (~1 wt.%) and Mg (~0.3 wt.%) occurred during processing. Thermal simulations qualitatively supported the experimental observations, indicating increased thermal retention and displacement with increasing preheating temperature. The results demonstrate that base plate preheating alone is insufficient to suppress hot cracking in EN AW 7075 and may promote alternative crack-growth mechanisms at elevated temperatures, highlighting the need for alternative alloy or process design strategies.