Polyimide Reinforced with Graphene/Metal Oxide Nanocomposites: Surface Degradation Study Under Atomic Oxygen.

Atomic oxygen in low Earth orbit erodes polyimide, increasing surface roughness and degrading performance. The reactive species scission polymer chains and remove surface material, exposing fresh sites that accelerate further attack and disrupt thermal, electrical, and mechanical functions. In this paper, we evaluate nanoscale reinforcements of polyimide with graphene and metal oxides under controlled atomic oxygen exposure equivalent to 145 days at a 550 km orbit. Graphene with a thickness of few nanometers and particle size less than 2 µm, and metal oxides zirconia, zinc oxide, and titania with particle size less than 100 nm were investigated. Hybrids containing graphene plus metal oxide at a 1:1 ratio and a total loading of 0.75 wt% increased roughness relative to neat polyimide, with graphene-zirconia showing a rise of +121 percent, graphene-zinc oxide +10 percent, and graphene-titania +20 percent. The behavior is consistent with agglomeration, incomplete dispersion, and interfacial mismatch that hinder uniform blocking of atomic oxygen and limit formation of protective oxygenated groups. In contrast, single-filler composites at 0.75 wt% reduced average roughness, with graphene lowering S