Effects of Alkali Modulus on Early-Age Performance and Hydration Mechanisms of Slag-Phosphogypsum Composite Alkali-Activated Materials.
Article in Materials (Basel, Switzerland), 2026. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors.
Funding
Abstract
The disposal of phosphogypsum has emerged as a significant challenge for the phosphorus chemical industry in China in recent years. Utilizing phosphogypsum in alkali-activated materials represents an effective approach to valorize this byproduct. The alkali modulus is a critical parameter affecting the performance characteristics of phosphogypsum-based alkali-activated materials. This study aims to investigate the effects of the alkali modulus on the early-age properties (setting time, fluidity, flexural strength, and compressive strength) and hydration mechanisms of slag-phosphogypsum composite alkali-activated materials (HSFP) across various slag-phosphogypsum-fly ash systems, thereby identifying the optimal alkali modulus. The findings demonstrate that an alkali modulus of 1.35 optimally enhances the mechanical performance of HSFP. At this specific modulus, the equilibrium between alkalinity and soluble silica availability facilitates complete hydration, resulting in a dense gel-crystal microstructure characterized by the highest C-(A)-S-H gel content (58.2%) after 28 days. The effect of the alkali modulus on mechanical properties is contingent upon the fly ash-to-phosphogypsum (FA:PG) ratio, whereas its effect on fluidity and setting time is negligible. The effect of alkali modulus on the strength of HSFP is significantly affected by the fly ash-to-phosphogypsum (FA:PG) ratio. At an FA:PG ratio of 4:6, the flexural strength initially decreases and then increases as the alkali modulus values increase, while the compressive strength shows a consistent upward trend. At FA:PG ratios of 1:5 and 1:9, the flexural strength increases linearly with the alkali modulus, whereas the compressive strength first rises and then experiences a slight decline. These results offer both theoretical insights and practical guidance for the optimization of phosphogypsum-based cementitious material formulations, thereby supporting their potential for large-scale application.