Mechanism-Informed Breakdown: Understanding Degradation by Controlling Voltage-Hold Patterns in Proton Exchange Membrane Water Electrolyzers.

Low catalyst loadings pose challenges to performance stability in proton exchange membrane (PEM) water electrolysis over extended operation. To study the impact of degradation mechanisms and voltage loss rates, different stress tests are applied to membrane electrode assemblies. Potential cycling conditions were observed to induce higher degrees of iridium (Ir) oxide crystallization, ionomer degradation, and catalyst layer (CL) thinning, which likely contributed to higher kinetic loss rates. On the other hand, while Ir migrating into the PEM (Ir band) generally impairs performance, the interconnected and more uniform Ir band formed under a constant 2 V hold may allow for Ir at the catalyst/membrane interface to remain electronically connected and kinetically accessible, as well as indicate greater Ir site access during the applied stressor. The 2 V hold also demonstrates improved kinetic durability through a lower Tafel slope, faster polarization kinetics, and reduced charge transfer resistance. In contrast, potential cycling caused the migration of disconnected Ir agglomerates into the membrane bulk and created a steady increase in charge transfer resistance, a more dramatic decrease in capacitance (46.7% loss), and significant damage to the surrounding ionomer, indicating a decline in both the quality and quantity of active sites in the anode CL. This work underscores the distinct degradation pathways associated with load holds versus cycling, highlighting the role of catalyst-ionomer interactions in kinetic performance and long-term stability. These insights can inform operational strategies for PEM electrolyzers powered by intermittent energy sources, aiming to minimize efficiency losses over extended operation.