Data-Driven AI Approach for Optimizing Processes and Predicting Mechanical Properties of Boron Nitride Nanoplatelet-Reinforced PLA Nanocomposites.

This research explores the optimization of mechanical properties and predictive modeling of polylactic acid (PLA) reinforced with boron nitride nanoplatelets (BNNPs) using data-driven machine learning (ML) models. PLA-BNNP composites were fabricated through injection molding, with a focus on how key processing parameters influence their mechanical performance. A Taguchi L27 orthogonal array was applied to assess the effects of BNNP composition (0.02 wt.% and 0.04 wt.%), injection temperature (135-155 °C), injection speed (50-70 mm/s), and pressure (30-50 bar) on properties such as tensile strength, Young's modulus, and hardness. The results indicated that a 0.04 wt.% BNNP loading improved tensile strength, Young's modulus, and hardness by 18.6%, 32.7%, and 20.5%, respectively, compared to pure PLA. Taguchi analysis highlighted that higher BNNP concentrations, along with optimal injection temperatures, improved all mechanical properties, although excessive temperatures compromised tensile strength and modulus, while enhancing hardness. Analysis of variance (ANOVA) revealed that injection temperature was the dominant factor for tensile strength (68.88%) and Young's modulus (86.39%), while BNNP composition played a more significant role in influencing hardness (78.83%). Predictive models were built using machine learning (ML) models such as Random Forest Regression (RFR), Gradient Boosting Regression (GBR), and Extreme Gradient Boosting (XGBoost). Among the ML models, XGBoost demonstrated the highest predictive accuracy, achieving R