Cracking-Resistance Mechanism of Fiber-Reinforced Coal-Based Solid-Waste Grouting Materials.
Article in Materials (Basel, Switzerland), 2026. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
9 authors.
Funding
Abstract
Grouting technology can be employed to repair cracks in an aquifer to maintain its stability; however, existing grouting materials tend to come with problems such as low flexural strength, poor cracking resistance, and the coupled effects of fiber reinforcement and sulfoaluminate cement (SAC) addition on hydrate evolution, and pore-refinement and crack-resistance mechanisms in coal-based solid-waste cementitious grouts remain insufficiently understood. In this paper, fiber-modified coal-based solid-waste grouting (F-CWG) materials were prepared by mixing different contents of sulfoaluminate cement (SAC) and different fibers. The mechanical strength, microstructure, hydration products, and pore evolution characteristics were analyzed by means of mechanical property tests, energy-dispersive X-ray spectroscopy (SEM/EDS), X-ray diffraction (XRD), thermogravimetric analysis (TGA), and nuclear magnetic resonance (NMR). The results show that the mechanical strength decreases at first due to insufficient early-stage hydration products. Specifically, the 28 d compressive and flexural strengths decrease from 15.34 MPa and 4.55 MPa at 0% SAC to 8.18 MPa and 2.99 MPa at 40% SAC but increase again to 13.36 MPa and 3.79 MPa at 60% SAC as the formation of ettringite (AFt) and C-S-H is promoted with higher SAC content. Among the tested fibers, a dosage of 0.6% generally improves mechanical strength and refines pore structure, with PVA and steel fibers showing the most pronounced effects. Our results reveal the mechanism behind the enhancement of cracking resistance in F-CWG materials, providing a scientific basis for grouting and water-preservation mining, and are of great significance in improving the utilization rate of coal-based solid waste.