Impact of Substrate Preheating on Weld Quality, Microstructure, Corrosion Resistance, and Mechanical Properties in Gas Tungsten Arc Welding of UNS S32750 Super Duplex Stainless Steel.
Article in Materials (Basel, Switzerland), 2026. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
8 authors.
Funding
Abstract
Super duplex stainless steels (SDSS) are materials known for their exceptional mechanical strength and high resistance to corrosion due to their dual- phase microstructure consisting of ferrite and austenite in roughly equal proportions. However, the Gas Tungsten Arc Welding (GTAW) process used to join SDSS often causes microstructural imbalances, mainly ferritic structures, or the formation of harmful intermetallic phases, which can weaken the material' s desirable properties. This study examines the effect of substrate preheating on the microstructure, mechanical properties, and corrosion resistance of UNS S32750 SDSS welds produced by GTAW. Preheating the substrate was considered as a strategy to improve phase balance in the fusion zone by extending the time within the ferrite- to- austenite transformation temperature range, thus slowing the cooling rates. Four conditions were tested: welding at room temperature (RT) and preheating to 100 °C (T100), 200 °C (T200), and 300 °C (T300). Welding parameters remained constant. The fusion zone microstructure was analyzed using metallographic techniques, while mechanical properties were evaluated through microhardness tests. Corrosion resistance was assessed with potential dynamic polarization in a 3.5% NaCl solution. The results showed significant improvements in microstructural balance with higher preheating temperatures. The austenite volume fraction in the fusion zone increased from about 16% at RT to 42% at T 300. Mechanical testing indicated a decrease in microhardness from 341 HV at RT to 314 HV at T 300, reflecting the increased austenite content and its associated toughness. Corrosion tests demonstrated enhanced resistance under preheated conditions, with T 300 exhibiting the highest corrosion potential and the lowest corrosion current, nearing the performance of the base metal. These findings suggest that preheating is a practical, cost- effective method for optimizing the GTAW process for SDSS, eliminating the need for expensive filler materials and stabilizing the microstructure elements.