Effect of ZnO on the pozzolanic activity and physico-mechanical properties of modified metakaolin cement mortar composites.
Article in Scientific reports, 2026. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
- Sustainable thermal comfort assessment of evaporative cooling systems in hot and arid climates.Scientific reports · 2026Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
2 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Metakaolin (MK) is commonly added to enhance the mechanical and durability properties of concrete. The pozzolanic activity of MK can be improved by calcining approximately ≈ 1 wt% ZnO with kaolin. However, the role of ZnO in enhancing the pozzolanic activity of MK remains unclear. The aim of this work is to investigate the surface modification of MK caused by ZnO that could enhance the pozzolanic activity of MK. ZnO-modified metakaolin (MMK) was prepared by calcination of kaolin powder (90 μm) with zinc carbonate basic equivalent to 1% by weight of ZnO, at 850 °C, and was analyzed by FTIR, XRD, and SEM techniques. The strength activity index according to ASTM C618, and the physico-chemical properties of blended cement mortars were measured at 28 days. Cement mortar samples were analyzed by FTIR, XRD, and SEM techniques. The XRD and FTIR results of MMK did not detect products of the interaction of ZnO and MK due to the detection limits. The SEM results illustrate the formation of uniform, non-aggregated (MMK) particles. The physico-chemical properties, strength activity index, FTIR, and XRD results of MK blended cement mortars indicated the higher pozzolanic activity of MMK. Whereas the SEM imaging shows the dispersion of cement particles coated with intense honeycomb-like C-S-H without being agglomerated in the case of MMK blended cement mortar. It was concluded that ZnO improves the pozzolanic activity by modifying the surface properties of MK during the calcination process as well as during the hydration process. The proposed mechanisms of surface modification of MK by ZnO were discussed. The addressed mechanism for visualizing the surface chemistry and microstructure of MMK paves the way for future studies on improving the pozzolanic activity of MK and the sustainability of cementitious-pozzolanic compositions.