ArticleThe journal of advanced prosthodontics2025
Effect of position within a blank and thermo-mechanical aging on fracture force and failure mode of strength-gradient multilayer zirconia crowns.
Article in The journal of advanced prosthodontics, 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
3 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
purposeThis study aimed to investigate the effects of blank position and thermo-mechanical aging on the fracture force of strength-gradient multilayer (SGM) zirconia crowns. MATERIALS AND
methodsEighty premolar SGM zirconia crowns (KATANA™ Zirconia YML) were assigned to eight groups (n = 10), based on four blank positions (1, 2, 3, and 4 mm below the top edge) and two conditions (with and without thermo-mechanical aging). Aging simulated five years of clinical service through 6,000 thermocycles (5℃ - 55℃) and cyclic fatigue (50 N, 1.2 Hz, 1,200,000 cycles). Fracture force was measured using a universal testing machine. Failure modes and fractographic features were examined. Data were assessed using two-way ANOVA, Bonferroni post hoc tests, independent t-tests, and Spearman correlation (
resultsFracture force was significantly influenced by both blank position and thermo-mechanical aging. Crowns from the 1 - 2 mm regions demonstrated significantly lower fracture force and more severe failure modes (Types I - V), while those from the 3 - 4 mm regions showed significantly higher fracture force and milder modes (Types I - III). Thermo-mechanical aging reduced fracture force in all groups, supported by fractographic analysis. A strong negative correlation existed between position depth and failure severity.
conclusionBoth blank position and thermo-mechanical aging significantly affected fracture force and failure behavior. Lower blank positions provide better mechanical performance and are recommended for posterior restorations. Conversely, upper blank positions-offering improved translucency-are suitable for anterior restorations where esthetics are prioritized. These findings offer clinically relevant guidance for optimizing strength and appearance in zirconia crown fabrication.