Fatigue Life Assessment of Notched PLA Manufactured Using FDM 3D-Printing Technique.
Article in Polymers, 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
2 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Fused Deposition Modeling (FDM) is an extensively employed additive manufacturing method for producing precise and complicated polymer models, with its industrial applications expanding under various loading conditions. A review of existing research highlights the insufficient investigation of the influence of geometric discontinuities in additively manufactured polylactic acid (PLA) members under fatigue loads. This study aims to analyze the combined effects of build orientation and geometric discontinuities on the static and fatigue performance and damage evolution of 3D-printed PLA. To achieve improved fabrication quality and minimize process-induced defects, the quasi-static tensile tests were conducted on specimens printed in on-edge orientation with a concentric infill pattern and the flat direction with a rectilinear infill pattern. The test results have shown that on-edge-printed objects have reduced micro-voids and improved layer bonding, resulting in a 19% increase in tensile strength compared to the flat-printed specimens. Consequently, this configuration was adopted for three specimen types, e.g., smooth, semi-circular edge-notched, and central-holed, tested under axial fatigue with a 0.05 load ratio. Fatigue test findings indicate that the stress concentration is more pronounced around central holes than near edge notches, leading to shorter fatigue life. This phenomenon is consistent with its effects under static tensile loading. Furthermore, using Digital Image Correlation (DIC) technique, damage initiation, progression, and failure mechanisms were analyzed in detail. According to fractographic analysis, the micro-voids in the 3D-printed specimens serve as potential regions for the initiation of multiple fatigue cracks. Additionally, the inherent internal defects can interact with geometric discontinuities, thereby weakening the fatigue performance.