Evolution of the Metallographic Structure of Additively Manufactured Ti-6Al-4V and Ti-6Al-7Nb Titanium Alloys.
Article in Materials (Basel, Switzerland), 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
3 authors.
Funding
Abstract
The aim of this study was to evaluate structural changes and their impact on the functional properties of Ti-6Al-4V and Ti-6Al-7Nb titanium alloys produced by L-PBF. In the as-built condition, these alloys, despite high strength due to the presence of metastable α' martensite, exhibit limited ductility. The samples were subjected to heat treatment at 850-1000 °C for 1 h, followed by aging at 500 °C for 4 h in an argon atmosphere. Analysis revealed a gradual microstructural transformation from the columnar structure characteristic of L-PBF to an equilibrium Widmanstätten microstructure. As a result of the decomposition of martensite and the formation of an α + β phase mixture, changes in microhardness and mechanical properties were observed. After heat treatment, the microhardness decreased by 15% for Ti-6Al-4V (from 427 ± 1 HV to 362 ± 25 HV) and by 12% for Ti-6Al-7Nb (from 408 ± 6 HV to 359 ± 15 HV). The Ti-6Al-7Nb alloy exhibited higher maximum elongation (7.7 ± 1.1%) than Ti-6Al-4V (4.8 ± 0.5%) due to a greater fraction of the β phase. The results highlight the critical role of the controlled α'→α + β transformation in tailoring the properties of titanium alloys and provide a basis for optimizing manufacturing processes for medical and aerospace components.