Phenol-Formaldehyde Adhesives Modified with Eucalyptus Lignin: The Advantages of Soda Lignin.
Article in Polymers, 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
Abstract
This study investigates the performance of phenol-formaldehyde adhesives containing Eucalyptus lignin as an extender in their formulation. A commercial phenol-formaldehyde resin was used, and five different types of lignin were tested: (1) kraft lignin precipitated with carbon dioxide, (2) kraft lignin precipitated with sulfuric acid, (3) soda lignin precipitated with hydrochloric acid, (4) soda lignin precipitated with sulfuric acid, and (5) a second soda lignin where the wood underwent a phosphoric acid extraction process prior to alkaline extraction. The lignins were used both unmodified and activated through three different processes: hydroxymethylation, phenolysis in an acidic medium, and alkaline phenolysis. Adhesives were formulated with substitution percentages of the base resin ranging from 10% to 60%, in addition to a reference adhesive that contained no lignin. Wooden test specimens were manufactured to determine the tensile shear strength. Results indicate that best performance is achieved when lignins are activated through hydroxymethylation and when soda lignin is used. Under optimal conditions, it is possible to replace at least 45% of the base resin with activated Eucalyptus soda lignin, which represents a reduction of at least 30% in the cost of the final adhesive. This substitution results in a 46% increase in adhesive strength compared to the base adhesive (without lignin). These findings suggest that the valorization Eucalyptus soda lignin could have significant economic and environmental benefits.