Effect of Preformed Polymeric Microspheres on the Frost Resistance of Low-Clinker Cementitious Composites with Fine Recycled Aggregate.
Article in Materials (Basel, Switzerland), 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
4 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Achieving adequate frost resistance in cementitious composites made with low-clinker binders remains challenging, as conventional air-entraining admixtures often show limited effectiveness in such systems. This study examines an alternative approach that involves incorporating preformed polymeric microspheres to create a stable air-void system and enhance freeze-thaw durability. Cementitious composites were prepared using a low-clinker binder containing fly ash and ground granulated blast furnace slag (GGBFS) as supplementary cementitious materials, with natural sand partially replaced by fine recycled aggregate derived from concrete waste. The influence of polymeric microspheres on workability, compressive strength, pore structure, and frost resistance was evaluated. Compared to the reference mixture (32.8 MPa), the mortar modified with polymeric microspheres exhibited clearly higher compressive strength-about 25% greater after 28 days-while the AEA-modified mixture showed a slight reduction. Total porosity measured by MIP was 18% for REF, 19% for AEA, and 17% for PPMThe results showed that adding polymeric spheres initially introduced a network of discrete voids that improved the material's resistance to early freeze-thaw cycles. However, due to the prolonged hydration of the low-clinker system, hydration products progressively filled the initially created voids after the partial degradation of the polymeric spheres. Consequently, the air-void system gradually disappeared, leading to a loss of frost resistance at later ages. After 100 cycles, the PPM mixture exhibited a 75% loss in flexural strength and a 35% loss in compressive strength, whereas the AEA mixture retained its durability, with compressive strength loss limited to 6%. This finding suggests that, although early tests may indicate improved performance, the long-term durability of low-clinker cementitious composites incorporating fine recycled aggregate cannot be reliably enhanced by preformed polymeric spheres alone.