Influence of Layer Thickness and Extrusion Temperature on the Mechanical Behavior of PLA-Flax TPMS Sandwich Structures Fabricated via Fused Filament Fabrication.
Article in Materials (Basel, Switzerland), 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
4 authors.
Funding
Abstract
Triply periodic minimal surface (TPMS) sandwich structures made from PLA, reinforced with flax fibers, offer a bio-based approach to lightweight design, but their performance is sensitive to material-extrusion parameters. This study investigates the combined effects of layer height (0.16, 0.24, and 0.28 mm) and extrusion temperature (200, 220 °C) on the flexural behavior of gyroid-core PLA-flax sandwiches. Six parameter combinations were fabricated by fused filament fabrication and tested in three-point bending to obtain flexural strength and strain at failure. Post-fracture optical microscopy related mesostructure and failure mechanisms to macroscopic response. The highest strength (≈23 MPa) was found at 0.28 mm/200 °C, while the greatest strain at failure (≈0.06 mm/mm) occurred at 0.16 mm/200 °C. Two-factor ANOVA showed the significant main and interaction effects of temperature and layer height on both metrics. Fractography revealed a transition from interfacial delamination at lower temperatures and thinner layers to a more localized, cohesive rupture as interlayer bonding improved with higher temperature and thicker layers. Complementary compression tests revealed a core-dominated cellular collapse, with first-collapse stresses ranging from 6.3 to 8.2 MPa and a significant dependence on layer height and temperature (ANOVA). A gate-to-gate sustainability assessment indicated that layer height dominates printing time, energy demand, and CO