Sample preparation induced artefacts in soft SAC solders from uncooled and cooled Argon ion milling.
Article in Scientific reports, 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
9 authors.
Funding
Abstract
Complex combinations of various materials in microelectronic packages pose challenges for sample preparation. Reliable cross-sectional sample preparation is critical for microstructural analysis, especially when utilising low-melting Sn-Ag-Cu (SAC) solders, which are easily deformed or damaged by mechanical grinding. Hence, this study explores the impact of femtosecond laser ablation for bulk material removal and subsequent Ar-ion milling for final cross-sectional polishing, comparing cooled and uncooled milling masks. We reveal that uncooled Ar-ion milling causes artefacts like increased surface roughness and fine Cu-rich structures due to surface heating combined with Cu redeposition on the preferentially milled, intruded SAC-surface. Cryogenic cooling of the milling mask to -100 °C reduces these effects, minimising curtaining and preserving microstructural details. However, we also show that cooled milling may result in the displacement of recrystallised grains at grain boundaries due to the thermal expansion anisotropy of β-Sn. Thus, milling parameters must be carefully tailored to the desired preservation of microstructure, cracks and strain.