A Study on Thin Cooling Layers Between the Cooling Channel and Cavity in the Injection Molding Process for Mold Temperature Control to Enhance Weld Line Flexural Strength in Plastic Products.
Article in Polymers, 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
5 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Weld lines in injection-molded plastics often act as structural weak points that reduce mechanical performance. Enhancing weld line strength is therefore essential to improve product reliability and service life. This study aims to develop and validate an injection mold system capable of localized cavity temperature control to strengthen weld line regions. A specialized mold with an integrated cooling layer was designed to enable rapid thermal response during molding. The Taguchi method was applied to optimize three key parameters-part thickness, melt temperature, and injection pressure-to maximize weld line flexural strength. Experiments based on an L25 orthogonal array revealed that weld line stress varied significantly across parameter combinations, with a maximum of 109.23 MPa. A subsequent validation test conducted under the optimal conditions (250 °C melt temperature, 1.5 mm part thickness, and 16 MPa injection pressure) achieved an enhanced weld line stress of 121.88 MPa, confirming the reliability of the Taguchi-based optimization. Among the factors studied, part thickness had the greatest influence, followed by injection pressure, while melt temperature had the smallest effect. These results demonstrate that combining cavity temperature control with systematic parameter optimization provides an effective strategy to enhance weld line strength in high-performance plastic components.