Simplified Fracture Mechanics Analysis at the Zinc-Adhesive Interface in Galvanized Steel-CFRP Single-Lap Joints.
Article in Materials (Basel, Switzerland), 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
2 authors.
Funding
Abstract
Adhesively bonded joints between galvanized steel and carbon fiber-reinforced polymers (CFRPs) are critical in modern lightweight structures, but their performance is often limited by failure at the zinc-adhesive interface. This study presents a parametric analysis to investigate the influence of key geometric parameters on interfacial cracking in a single-lap joint (SLJ) configuration, employing a simplified analytical methodology based on Interface Fracture Mechanics (IFM). The model combines the Goland-Reissner approach for estimating crack-tip loads with highly simplified, constant shape functions to calculate the energy release rate (Gint) and phase angle (ψ). To provide a practical reference, experimental data from shear tests on S350 GD galvanized steel bonded to CFRP were used to estimate the range of interfacial fracture toughness for this material system. The parametric results demonstrate that, for a constant load, increasing the overlap length reduces the crack driving force (Gint), while increasing the adhesive thickness raises it. Crucially, the model indicates that a thicker adhesive layer shifts the fracture mode from shear- to opening-dominated, a trend consistent with the established mechanics of SLJs, where increased joint rotation amplifies peel stresses. The study concludes that while the use of constant shape functions limits the model's quantitative accuracy, this simplified analytical framework effectively captures the qualitative influence of key geometric parameters on the joint's fracture behavior. It serves as a valuable and resource-efficient tool for preliminary design explorations and for interpreting experimentally observed failure trends in galvanized steel-CFRP joints.