Effect of Hydrothermal Aging on Mechanical and Microstructural Properties of Zirconia Ceramics.
Article in Nanomaterials (Basel, Switzerland), 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
2 authors.
Funding
Abstract
The mechanical and microstructural properties of monolithic zirconia ceramics are significant factors for their long-term clinical performance. This study aims to investigate the effects of hydrothermal aging on these properties for the 3Y-TZP, 4Y-TZP, and 5Y-TZP formulations. Specimens were prepared from 3 different zirconia blocks: 3Y-TZP (HT), 4Y-TZP (ST), and 5Y-TZP (XT). Half of the specimens were aged in an autoclave (134 °C, 2 bar, 5 h) while the others remained as controls. Three-point flexural strength, Vickers hardness, and surface roughness tests, as well as XRD, AFM, and SEM/EDS analysis, were performed. The material type significantly affected the flexural strength, Vickers hardness, and surface roughness. Aging did not significantly affect the flexural strength or surface roughness but reduced the Vickers hardness in the 3Y-TZP sample. The 3Y-TZP and 5Y-TZP samples displayed the highest and lowest flexural strength, respectively. In the non-aged groups, 3Y-TZP and 5Y-TZP exhibited higher hardness than 4Y-TZP, and after aging, 3Y-TZP displayed the lowest hardness. Further, 5Y-TZP showed the highest surface roughness before and after aging. XRD revealed an increased monoclinic phase in the aged 3Y-TZP and 4Y-TZP. No monoclinic phase was observed in 5Y-TZP. According to AFM measurements, aging led to a smoother surface in 3Y-TZP but increased roughness in 4Y-TZP and 5Y-TZP. SEM/EDS revealed changes in the elemental compositions following aging. According to the results of this study, different material formulations affect the mechanical behavior and microstructural properties of monolithic zirconia ceramics. Further, hydrothermal aging displayed effects on the Vickers hardness and phase transformations.