Manufacturing Technology and Mechanical Properties of Novel Pre-Impregnated Coatings as Applied to FRP "Sandwich" Composites.

This article presents the manufacturing technology and mechanical properties of innovative pre-impregnated coatings (PCs). The base materials for PC are powders of metal oxides, non-metals, minerals and thermoplastic non-wovens. PC can be used in the manufacture of composites by methods such as vacuum infusion, autoclave curing or hand lamination. This is possible due to the novel PC structure consisting of a functional layer (FL) and a backing layer (BL). PCs are flexible so that they can be used on curved surfaces. In this work, five types of PC were subjected to a uniaxial tensile test. Depending on the powder used, failure force values ranging from 24.61 N to 28.73 N were obtained. In the next step, the pre-impregnated coatings were applied as a coating in "sandwich" composites made by vacuum infusion, which were subjected to three-point bending (3-PB) and adhesion tests. 3-PB tests proved that the coating remained integral with the substrate, even under high flexural deformation, while the adhesion achieved was in the range of 0.95 MPa to 1.57 MPa. PC can be used in many engineering products, e.g., for the coating of façade panels, roof tiles, automotive parts or rail vehicles, etc.