Machinability of Vitrified Semi-Finished Products: Chip Formation and Heat Development at the Cutting Edge.
Article in Polymers, 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Fibre-reinforced composites are facing new challenges in the context particular in sustainability and recyclability. Vitrimers could be useful as new matrices to support the increase in sustainability. Due to their high strength, which is comparable to that of thermosets often used in composites, and their covalent adaptive networks, which make them reshapeable for scaled-up manufacturing and recycling purposes, they are very useful. Orthogonal cutting is used for precise reshaping and functional integration into carbon fibre reinforced plastics. Vitrimers could improve processing results at the cutting edge as well as surface quality thanks to their self-healing properties compared to brittle matrices, as well as enabling the recycling of formed chips and scrap. This study showcases the manufacturing of a carbon fibre-reinforced vitrimer using 4-aminophenyl disulfide as a hardener, with vacuum-assisted resin infusion. The temperature of chip formation and the cutting parameters are then shown for different fibre orientations, cutting widths and speeds. The observed cutting forces are lower (less than 140 N) and more irregular for fibre orientations 45°/135°, increasing with cutting depth, and fluctuating periodically during machining. Despite varying cutting speeds, the forces remain relatively constant in range between 85 N and 175 N for 0°/90° fibre orientation and 50 N and 120 N for 45°/135° fibre orientation, with no significant tool wear observed and lower-damage depth and overhanging fibres observed for 0°/90° fibre orientation. Damage observation of the cutting tool shows promising results, with lower abrasion observed compared to thermoset matrices. Microscopic images of the broached surface also show good quality, which could be improved by self-healing of the matrix at higher temperatures. Temperature measurements of chip formation using a high-speed camera show a high temperature gradient as cutting speeds increase, but the temperature only ever exceeds 180 °C at cutting speeds of 150 m/min, ensuring reprocessability since this is below the degradation temperature. Therefore, orthogonal cutting of vitrimers can impact sustainable composite processing.
Indexed as
Identifiers
What OpenQuestion holds
Registered trials
Read under generation 80e0d062 · epoch 390. Bibliography from PubMed, PubMed Central and OpenAlex; grants from NIH RePORTER; trial links from ClinicalTrials.gov; estimates, votes and beliefs from the OpenQuestion graph.