Changes in the flexural strength and surface characteristics of different zones of multilayered translucent zirconia during aging process.
Article in Journal of materials science. Materials in medicine, 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 3 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
3 citing papers in PubMed.
- Load-bearing capacity and Weibull characteristics of inlay-retained fixed dental prosthesis: Effect of zirconia type, bonded substrate and aging.Clinical oral investigations · 2026Article
- Characterization of Multilayer Structure-Graded Dental Zirconias.Bioengineering (Basel, Switzerland) · 2026Article
- Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
Abstract
objectivesThis study evaluated the mechanical and surface characteristics of the transition zone of multilayered translucent zirconia (TZ) after aging and analyzed the correlation between the 4-point bending flexural strength (4PBFS) and biaxial flexural strength (BFS) in each zone.
methodsTraditional (3Y-TZP of LT; L, 4Y-TZP of MT; M) and multilayered TZ (5Y-TZP of MT Multi; T, 3Y/5Y-TZP of Prime; P, 4Y/5Y-TZP of Prime esthetic; E) IPS E.max ZirCAD blocks were used to fabricate 525 disk-shaped and 300 bar-shaped specimens. Specimens were separated into three groups, aged in an autoclave at 134 °C under 0.2 MPa for 0 h, 5 h, and 10 h. The mechanical and surface characteristics of the transition zone in multilayered TZ were analyzed, following statistical analyses (α = 0.05).
resultsL showed the highest 4PBFS and BFS, irrespective of aging. Consistent correlations between the 4PBFS and BFS were found in all groups. L showed the highest Weibull characteristic strength under all conditions. T showed the highest nanoindentation hardness and Young's modulus, and the Vickers hardness of L and P were lower than other groups. Aging led to surface uplifts and microcracks caused by phase transformation, particularly in L and P.
conclusionsThe flexural strength of 3Y/5Y-TZP and 4Y/5Y-TZP was comparable to that of 3Y-TZP and 4Y, 5Y-TZP respectively, regardless of aging. Surface roughness showed a marked increase after aging in 3Y-TZP and 3Y/5Y-TZP. Furthermore, the interaction between yttria content and aging was evident across all mechanical and surface characteristics, except for flexural strength.