Assessing the Performance and Lifetime of Cellulose Nitrate Lacquer on Silver.

Silver tarnish is a major issue in many heritage institutions. Applying lacquer is frequently used when preventive conservation approaches are limited. The service lifetime of the lacquer has a strong impact on resources and sustainability. Little systematic work has been published on this. This work explores three thresholds on lifetime-visual, reversibility, and loss of protection. It uses thermodynamic modelling to predict lacquer lifetime from aging at four temperatures. Samples on sterling silver with Frigilene lacquer were used and aging was assessed with a Bruker Alpha FTIR using external reflectance. The FTIR ratio of produced carbonyl peak to nitrate peaks was used to quantify the aging. The commonly used C-O-C peak was found to suffer from dispersion in a high proportion of samples, so could not be used in this study. The results were compared with measurements of lacquer on silver objects displayed in showcases and from store (with almost no light exposure). Spectra were obtained with the Bruker Alpha or an Inspect infra-red microscope. Autocatalytic effects through concentration of emitted nitrogen oxide gases have also been explored using diffusion tubes and gas ingress analysis. No significant concentration was observed. The thresholds were clearly established, and the model produced similar results to the natural aging studied.