Macro-Microscopic Characterization and Long-Term Performance Prediction of Polyvinyl Chloride Under Hydrothermal Aging Based on Creep Behavior Analysis.
Article in Polymers, 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed.
- Role of CaCOMaterials (Basel, Switzerland) · 2026Article
- High-Temperature Tensile and Creep Properties of Highly Strong Heat-Elongated Polypropylene.Polymers · 2026Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
5 authors.
Funding
Abstract
The creep behavior of rigid polyvinyl chloride (PVC) in hydrothermal environments can compromise its long-term stability and load-bearing capacity, potentially leading to deformation or structural failure. Understanding this degradation is critical for ensuring the durability and safety of PVC in engineering applications such as pipelines and building materials. In this study, accelerated hydrothermal aging tests were carried out on PVC under controlled conditions of 60 °C and 90% relative humidity (RH). Short-term tensile creep tests at four different stress levels were conducted both before and after aging. Microstructural changes associated with the PVC's creep behavior were analyzed using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and other microscopic characterization techniques. These analyses provided a detailed microscopic interpretation of how hydrothermal exposure and applied loads influenced the macroscopic creep performance of the PVC, thereby elucidating the correlation between its macroscopic mechanical behavior and microstructural evolution. By applying the time-stress equivalence principle and the time-aging equivalence principle, the short-term creep behavior was characterized to predict long-term performance. The accelerated characterization curve can effectively predict the creep behavior of PVC under a stress level of 16 MPa over approximately 6.5 years in an environment of 60 °C and 90% RH. At the same time, the master creep modulus curve of PVC under any aging duration and stress level can be established under the specified environmental conditions of 60 °C and 90% RH. Long-term creep curves were fitted using a locally structured derivative Kelvin model, demonstrating that this model can effectively simulate the long-term creep behavior of PVC under hydrothermal conditions. The results indicate that at a stress level of 16 MPa, PVC is expected to undergo creep damage and failure after approximately 15 years in such an environment. These findings provide a critical reference for assessing the long-term performance of PVC in hydrothermal environments.